1. Inspection and treatment before pickling

检查铁艺工件是否具备本厂镀锌的工艺孔（排气、出入锌夜、吊挂），铁艺工件表面的锈蚀程度，表面覆盖物能否被盐酸除去（如有油漆、油脂等应采用火烧、打磨、碱洗等法除去）。

Check whether the iron work piece has the galvanized process hole of the factory (exhaust, zinc in and out, hanging), the degree of corrosion on the surface of the iron work piece, and whether the surface covering can be removed by hydrochloric acid (if there is paint, grease, etc., it shall be removed by fire, grinding, alkali washing, etc.).

2.脱脂（碱洗）

2. Degreasing (alkali washing)

配有加热设备，消除铁艺工件表面的油脂、涂料等。

Equipped with heating equipment to eliminate grease, coating, etc. on the surface of iron workpieces.

3.水洗

3. Water washing

清除铁艺工件表面的碱水及附着物。

Remove alkali water and attachments on the surface of wrought iron workpieces.

4.酸洗

4. Pickling

除去铁锈、氧化皮等其它表面覆盖物。

Remove rust, scale and other surface coverings.

5.酸洗后检查处理：

5. Inspection and treatment after pickling:

酸洗效果是否理想，如酸洗不充分，再次酸洗，如果酸洗前处理不彻底，需重新处理后再次酸洗。

Whether the pickling effect is ideal. If the pickling is insufficient, pickling shall be carried out again. If the treatment before pickling is not complete, pickling shall be carried out again after re treatment.

6.水洗

6. Water washing

除去铁艺工件表面的酸水及其它附着物。

Remove acid water and other attachments on the surface of iron work pieces.

7.上助镀剂

7. Plating aid

再次清洗工件表面，保证表面在镀锌之前不在生锈。

Clean the workpiece surface again to ensure that the surface does not rust before galvanizing.

8.烘干

8. Drying

提高铁艺工件温度，避免铁艺表面水分过多，在镀锌时发生爆炸。

Raise the temperature of wrought iron workpiece to avoid excessive moisture on the surface of wrought iron and explosion during galvanizing.

9.热浸锌

9. Hot dip galvanizing

工件浸泡于440℃-470℃熔融的锌液中，达到一定时间后提出，铁艺工件表面被获得一层锌铁合金层和纯锌层镀层。

After the workpiece is immersed in molten zinc at 440 ℃ - 470 ℃ for a certain time, a layer of zinc iron alloy layer and pure zinc layer are obtained on the surface of iron workpiece.

10.钝化

10. Passivation

提供工件表面抗大气的腐蚀性能，减少或延长白锈出现的时间。

Provide atmospheric corrosion resistance of workpiece surface to reduce or prolong the time of white rust.

11.冷却

11. Cooling

防止工件激冷回缩，产生集体组织开裂。

Prevent the workpiece from chilling and retracting, resulting in collective structure cracking.

12.检验

12. Inspection

镀层的检验和测定，工件的外观检查。

Inspection and measurement of coating and appearance inspection of workpiece.